道恩集團有(yǒu)限公(gōng)司
HIPS材料廣泛應用(yòng)各種擠出、注塑類産(chǎn)品中(zhōng)。由于韌性不足，部分(fēn)HIPS制品存在低溫開裂、打螺絲爆裂等問題。我司増韌母料采用(yòng)高分(fēn)子量的丁二烯類三元共聚物(wù)為(wèi)主要原材料，改性後經雙螺杆擠出造粒，可(kě)以有(yǒu)效提高HIPS的沖擊強度和拉伸斷裂伸長(cháng)率，解決制品韌性差、脆裂、打螺絲爆裂等問題，添加在HIPS中(zhōng)，有(yǒu)效提高沖擊強度，可(kě)部分(fēn)替代ABS制件，降低成本，适用(yòng)于各種擠出、注塑制品，具(jù)有(yǒu)廣闊的市場應用(yòng)前景。
Hips materials are widely used in various extrusion and injection products. Due to lack of toughness, some HIPS products have the problems of low temperature cracking and screw cracking. The Toughening Masterbatch of our company uses high molecular weight butadiene terpolymer as the main raw material. After modification, it is extruded and granulated by twin-screw, which can effectively improve the impact strength and tensile elongation at break of HIPS, solve the problems of poor toughness, embrittlement, screw cracking and other problems of products. When added to hips, it can effectively improve the impact strength, partially replace ABS parts, reduce the cost, and is suitable for extrusion injection molding of various products has a broad market application prospects.
冰箱擠出闆材、各類注塑家電(diàn)制件、HIPS玩具(jù)、日用(yòng)品等的性能(néng)提升。
The performance improvement of refrigerator extruded board, all kinds of injection molded home appliances, HIPS toys, daily necessities, etc.
1、熔融指數(200℃，5Kg)：20-50g/10min；
2、提高HIPS的沖擊強度并保持其它機械性能(néng)基本不變；
3、解決制品韌性差，低溫脆裂，打螺絲爆裂等問題；
4、添加在高光HIPS中(zhōng)，提高沖擊強度，替代ABS外觀件，降低成本；
5、不會影響高光HIPS的光澤度；
6、易添加，可(kě)以靈活調整比例，解決不同的韌性問題。
1.MFI (200 ℃, 5kg): 20-50g / 10min;
2. Improve the impact strength of HIPS and keep other mechanical properties unchanged;
3. Solve the problems of poor toughness, low temperature embrittlement, screw bursting, etc;
4. Add in high gloss hips, improve impact strength, replace ABS appearance parts, reduce cost;
5. Does not affect the glossiness of high gloss HIPS;
6. Easy to add, flexible to adjust the proportion, to solve different toughness problems.
ZQ 21499D低成本増韌母粒，效果好，價格低，分(fēn)散好。
ZQ 21144D増韌着色一體(tǐ)，不用(yòng)再添加色母料，減少工(gōng)序，降低成本。
ZQ 21499d low cost Toughening Masterbatch, good effect, low price and good dispersion.
ZQ 21144d is toughened and colored as a whole, and there is no need to add color masterbatch to reduce the process and cost.
向右滑動表格查看更多(duō)内容
|
Property |
測試方法 Test method |
測試條件 Test condition |
單位 Unit |
HIPS1173原料 HIPS1173 raw, material |
ZQ21235D |
ZQ21499D |
ZQ2144D |
|
MFR |
ISO 1133 |
200℃, 5 kg |
g/10 min |
/ |
45 |
25 |
20 |
|
Density |
ISO 1183 |
23℃ |
g/m3 |
1.05 |
0.92 |
1.332 |
1.45 |
|
Ash% |
|
|
|
|
0.01 |
28 |
23.5 |
|
拉伸強度Tensile strength |
ISO 527 |
50 mm/min |
MPa |
23.67 |
22.48 |
21.69 |
21.96 |
|
斷裂伸長(cháng)率 Elongation at break |
ISO 527 |
50 mm/min |
% |
80.2 |
83.8 |
79.2 |
80.8 |
|
彎曲強度 Bending strength |
ISO 178 |
2 mm/min |
MPa |
30.32 |
29.97 |
29.38 |
29.65 |
|
彎曲模量 Flexural modulus |
ISO 178 |
2 mm/min |
MPa |
1357 |
1338 |
1319 |
1332 |
|
懸臂梁缺口沖擊強度Notched impact strength of cantilever |
ISO 179 |
4mm, 23℃ |
kJ/m2 |
11 |
13.5 |
13.2 |
13.3 |
|
(Note: the product can effectively reduce the cracking rate of refrigerator inner tank after verification by customers. The above data are typical experimental values for reference only（注：産(chǎn)品經客戶驗證可(kě)有(yǒu)效降低冰箱内膽開裂率，上述數據為(wèi)實驗典型值，僅供參考，不作(zuò)為(wèi)正式質(zhì)保承諾。） |
|||||||
使用(yòng)說明：産(chǎn)品的典型添加比例為(wèi)4%-10%，客戶可(kě)以根據増韌實際需求進行适量添加，按需求配比與其他(tā)原材料輔料混合均勻後即可(kě)使用(yòng)。
Instructions for use: the typical adding proportion of the product is 4% - 10%. The customer can add appropriate amount according to the actual demand for toughening, and use the product after it is evenly mixed with other raw materials and auxiliary materials according to the demand ratio.
青島潤興塑料新(xīn)材料有(yǒu)限公(gōng)司